To Spyderco -

I am bit disappointed. You effectively ban me by making my posts invisible for everybody but me, but without warning, without explanation, I do not feel like I broke any rules or anything. Only reason I see is you do not like my posts. So seems like Spyderco only like to hear pleasant cry about how great their knives is. I see that before, it will not lead to any good.

This is I guess biggest step down degradation path Spyderco taking right now. And I have no any respect to Sal, no more.

Good day then.

This actually mean that Spyderco forum does not have any informational value - reading it is like reading promotional materials, but not with some marketing drones, but by fanboys without any actual knowledge and without any responsibility.

For example I bought H1 knife after reading that it has so called working hardening written by some overexcited fanboy. Of course nothing like that ever existed, but I already bought knife.

So it is clear for me now that reading Spyderco forum trying to learn about knives would not be a good idea.
---------------------------------------------------------------------------------------------------------------------
Spyderco меня фактически забанила на форуме - зделано это было самым трусливым способом. Никто ничего мне не сказал и не объяснил не предупредил - мои посты мне видны, но если зайти не под моим аккаунтом - то их не видно. То есть фактичкски меня забанили и на Spyderco форуме, опять же без каких либо нарушений с моей стороны - просто мои посты их не устраивают вот они их и сделали невидимыми,  потихому.

Это прекрасный пример как дела делаются в странах с развитой демократией...

Хотя топорно сработали. Вот здесь моих постов не видно, но видны цитаты в постах других:

http://www.spyderco.com/forums/showthread.php?58604-Steel-Junkies-A-new-laminate-S-90V-clad-with-cpm-154-cm-FYI/page7

В правилах форума кстати про это ничего не написано. Они могут удалять, но здесь идет речь о тотальной изоляции, причем таким образом что бы участник не заметил, что его фильтруют.

Посты которые изолированы таким образом никак правил форума не нарушают:

Posts which Spyderco made invisible for all participants of the forum, but me - I check rules, I do not see where did I broke any:

http://www.spyderco.com/forums/showthread.php?58953-New-to-spyderco-need-some-help

Hitachi Aogami - blue label steel is one of two major steels (other one Shirogami - white label steel)
of choice for top custom knives in Japan. In US everybody came up with different names - now it is
super blue somehow, but it is just because Hitach pack it in blue paper. Japanese lately tend to
laminate it with stainless steel to make it less vulnerable, I wish Spyderco learn how to do that.

In general this is high carbon steel with W added to make it easyer to HT - Shirogami HT require
exceptional skills from craftsmen it has quite thin temperature window not to overheat and they measure
temperature by color of heated steel, tungsten widen this window and add a little edge holding over
Shirogami if HT done properly.

As high carbon steel it has better edge holding and much cheaper then top stainless steels with exotic
composition and super modern production process. Unfortunately this does not make knife any cheaper
but it will hold edge well.

High carbon steel also means not just corrosive but high corrosive steel.

Non stainless steel is more vulnerable on pocket knives, because spine even with closed blade always
exposed. Especially for touch and in many case it corrode even without use or even with being taken
care after use - just by holding closed or in the pocket. For this reason I made little pouch to carry non
stainless pocket knives.

http://www.spyderco.com/forums/showthread.php?58940-diamond-rods-cleaning-and-coated-blades

In general diamonds can stand any coating just fine. I sharpen a lot of blade with different coating - no problem.
Only problem I know with diamonds is rapid wearing if push too hard - but this depends on diamonds quality.
There is monocrystalline and polycrystalline diamonds. First is whole diamonds welded to steel plate with Nickel,
like layer of Nickel on top of steel plate with diamond stick out of it. Second - polycrystalline is when small diamond
particles kind of baked together to form bigger particles, so it is not solid piece but rather bunch of small stick
together. Of course solid diamonds are much stronger and last much longer - a lot longer.

I am not sure what kind of diamonds Spyderco uses and who is their subcontractor for this rods.

I am not aware of any other cleaning procedure for diamonds then one you already mentioned.

---

Stripping chemically coating will expose unfinished blade surface. Manufacturers save a lot on
polishing by hiding raw, after grind blade under one or other coat. I am trying to avoid knives
with coating - it looks nice NIB but with use it get scratched, fall off etc - depends on quality
and looks ugly in result. And only because it is easier to coat then polish.

You may strip it, but then you will have to polish it. Reason that it is not left simple unpolished
by manufacturers who do not like to polish is hygiene and corrosion. If surface is not polished it
will attract water and dirt and your blade will be dirty, not healthy and corrodes. This is why they
have to coat it. Stripping coat of left you with vulnerable unhealthy blade so you will have to polish
it yourself, which is not very easy job to do properly.

http://www.spyderco.com/forums/showthread.php?58936-How-strong-is-the-Chris-Reeve-Integral-Lock

Only benefit of Integral lock - version of Walker liner lock over other liner lock is that you may manually by your own fingers push lock bar in and so make lock stronger.
It does wear same as back lock, but if liner lock made right it will work with some wear just going deeper in, you may check what part of blade back and lock are engaged
in the locking.

Liner lock may loose if lock bur got bended which make it shorter, lock edge may deform - nothing really specialy strong about it.
Some made bar thick, some use hardened steel bit on the end of the bar, but there is nothing special in this lock design which
make it stronger then major competing locking mechanisms.

Do not relay on marketing materials too much - they tend to hype things a bit.

Flipping may put bit more wear then slow opening, but most likely you may notice this difference in few hundred years of normal
use...

---------------------------------------------------------------------------------------------------------------- 
Это конечно неприятно, что говорить. Однако интересно как это все было сделано - ведь не просто забанили, а скрытно, тайно, трусливо сделали невидимым. Знают что не правельно поступают вот и изощьряются - бояться.

К этому еще добавлю что вся дискуссия о тестировании Милитари уральскими ножелюбами была целиком удалена - я по крайней мере ничего такого не нашел.

Добавлю к этому еще мои давние безуспешные попытки найти дискуссию где Сал весьма грубо осаживал JapanSteel - инженера металлурга из Хитачи. Или резкий ответ Сала на мой вопрос от 2004 года где я интересовался - почему они не используют CPM M4 -  тогда Сал сказал что типа еще чего не хватало - нашему отделу гарантии отвечать на запросы клиентов у которых клинки заржавели... Становиться абсолютно понятно что никакой неудобной для Spyderco информации найти на этих форумах не получится.

В результате никакой ценности в них нет вообще, поскольку найти там можно только рекламные материалы, но написанные не маркетинговыми дронами, а экзальтированными фэнбоями, у которых не только какие либо знания отсутствуют, но и нет никакой ответственности. Я вот прочитал на форуме про рабчую закалку - тиа чем больше режешь сталью H1 - тем она тверже становиться и купил себе нож с ней. Однако как оказалось все это просто почудилось какому то перевозбужденному фэнбою.

Так что пытаться чего либо узнать и чему либо научиться на форумах Спайдерко лучше не стоит. Там все схвачено не хуже чем в министерстве Правды из утопии Оурэла.